In this study, to improve the interfacial bond strength of cast iron-aluminum dissimilar materials, graphite was removed to a certain depth from the cast iron surface through de-graphitization heat treatment. As the heat treatment time increased, the depth at which graphite was removed increased, showing a linear relationship between the heat treatment time and depth. Aluminum was filled to a certain depth on the de-graphitized cast iron surface through die-casting method, and no intermetallic compounds were formed on the cast iron-aluminum interface. The interfacial bonding strength showed a value of 90 MPa regardless of the heat treatment time, which is very high compared to the 12MPa bonding strength of the material without de-graphitization heat treatment. This result is thought to be due to the mechanical bonding of the undercut structure as the liquid aluminum, penetrated by the high pressure die-casting process, solidified in the de-graphitized region of the cast iron.

Aluminum alloys, Gray-iron, De-graphitization time, De-graphitization depth and Interfacial bonding strength