For enhancing the mechanical properties of LTE (low thermal expansion) cast steel, systematic researches have been carried out. The effects of alloying elements such as vanadium, molybdenum and carbon on the hardness and linear thermal expansion coefficient were investigated. In the range of carbon, addition of 1.73 wt% carbon caused hardness increase due to the formation of eutectic carbide having high hardness but over the range of 1.73 wt% carbon, hardness was decreased. Thermal expansion coefficient increases with carbon contents. In the LTE cast steel containing 0.6 wt% carbon, hardness increased up to 1.96 wt% vanadium addition. But over the range of 1.96 wt% vanadium hardness was decreased by coarse eutectic carbide. Thermal expansion coefficient of LTE cast steel containing 0.6 wt%carbon moderately increased with increasing vanadium contents. There was no significant variation of hardness and thermal expansion coefficient according to molybdenum content in LTE cast steel.