한국주조공학회지 (18권5호 488-493)

Mechanical Properties and Corrosion Resistance of CP-Ti and Ti Alloy for Dental Implants

인공치근용 CP-Ti과 Ti 합금의 기계적 성질 및 내식성

Yeon-Wook Kim, Chong-Pyoung Chung*

Keimyung University, *Seoul National University

Abstract

Commercially pure titanium(cp-Ti) and Ti-15wt%Zr-4wt%Nb-4wt%Ta alloy were melted in vacuum induction furnace. According to the chemical analysis, the content of carbon was above ASTM standard in the cast ingots because of using graphite crucible. The TEM micostructures of cp-Ti and Ti alloy shows that chemically stable TiC precipitates distribute in α-Ti matrix. In order to examine the properties of cp-Ti and Ti-Zr-Nb-Ta alloy for dental applications, mechanical properties and corrosion resistance were investigated. The anodic polarization properties of Ti- Zr-Nb-Zr alloy were almost same as that of cp-Ti in 1% lactic acid. However, as the results of the anodic polarization test in 5% HCl, it was known that Ti-Zr-Nb-Zr alloy showed a rapid decrease in current density at higher potential in comparison with cp-Ti. The yield stress and tensile strengh in Ti-Zr-Nb-Ta were σо‚₂=623 MPa , σt.s=708 MPa and these results showed 30% increase in yield stress in comparison with cp-Ti.

Keywords