Molybdenum ingot of 50mm in diameter were obtained from sintered Mo bars by EB drip melting technique. Macroscopic observation of EB remelted ingot indicates that coarse and columnar grains grow in the direction parallel to ingot pulling direction. This can be explained by slow solidification (3mm/min), large temperature gradient and heat flow to this direction. The orientation of columnar structure was found to be <110>, <200> and <211> by the analysis of X-ray diffraction patterns. The contents of typical metallic impurities in Mo sintered bar are 1.2ppm Cr, 3ppm Fe, 44ppm Zr, 150ppm W. Most of metallic impurities were reduced below the order of ppm except zirconium and tungsten by the selective evaporation. In the removal of nonmetallic impurities, oxygen and carbon impurities were lowered from 120 to 6ppm and from 157 to 106ppm, respectively, after first melting. Although the purification effect was not significant with the number of remelting, Vickers hardness was reduced from 217 to 195 and 184 in sequence with increasing the number of remelting.