The single crystal of CdTe was grown by modified 6 zone Bridgman method under the conditions of excess Te and excess Cd. To prevent the constitutional supercooling, the crystal growth was done under the temperature gradient of 17℃/cm in front of the solid /liquid interface and the growth rate was 3mm/hr. The grain morphologies and the growth mechanism were investigated in excess Te and excess Cd conditions. The grain size of excess Te crystal was increased with an increase of the distance from the tip but, in the case of excess Cd crystal, single crystal was not obtained because of the cavities due to the excess Cd vapors so that the grain size was not increased with an increase of the distance from the tip. In addition, the growth of single crystal of CdTe was done with repeated necking ampoule. It was found that the necking had no effects on the grain selection because the cavities trapped in the necking portion acted as heterogeneous nucleation sites.