Effect of Special the Heat Treatment on the Strength and Toughness in a Multi-phase(Ferrite-Bainite-Martensite) Ductile Cast Iron
3상(相) 혼합조직(混合組織) 구상흑연주철(球牀黑鉛鑄鐵)의 강인화(强引化)에 미치는 특수열처리(特殊熱處理)의 영향(影響)에 관(關)한 연구(硏究)
Hyun-Soo Choi, Sug-Won Kim
Chonbuk Nation University
This study is aimed to investigate the effect of cyclic heat treatment which is special heat treatment on the strength and toughness in Multi-phase(Ferrite-Bainite-Martensite) Ductile cast Irons. Spceimens were austenitized at eutectoid transformation temperature range(α+δ) for 30min and austempered at $300℃ and 400℃ for different holding times, and then quenched in ice water to obtain the multi-phase(Ferrite-Bainite-Martensite) structure from various prior structures, which was obtained by various cyclic heat treatments. As the number of cycle in cyclic heat treatment increased, volume fraction of pearlite increased and the its morphology was refined. As the number of cycle in cyclic heat treatment increased, the multi-phase(Ferrite-Bainite-Martensite) was dispersed in whole matrix as refined island phase. Particularly, martensite among the multi-phase gradually became a spherical shape. Good combination in impact energy and tensile strength was detained in 840℃-300℃-15min condition after 10 cycles in cyclic heat treatment, and its multi-phase volume fraction is Ferrite(50%)-Martensite(l3%)-Bainite(37%).