한국주조공학회

This study has been carried out to investigate the difference of rolling life and rolling wear characteristics for various high strength ductile iron castings under unlubricative dry rolling condition by Amsler type wear test with 9.09% sliding ratio. The tensile strength of the castings have been obtained 80, 90 and 100kg.f/mm^2 as cast-state with pearlitic, bainitic and martensitic matrix structures alloyed with Mo, Cu and Ni. It has been found that the amount of rolling wear is decreased when the tensile strength and hardnees of the castings are increased. The amount of rolling wear is increased, when the maximum compressive stress are increased. The maximum weight loss ratio of rolling wear of the castings are same at the 70000 numbers of revolution with out the maximum compressive stress.