In this study, the properties of Zr-14Cu-7.5Ni-2.6Al wide ribbon with amorphous structure and properties were analyzed using Hall effect, SEM-EDX, and XRD. Made by melt spinning method, this Zr-14Cu-7.5Ni-2.6Al based alloy ribbon is not more than 96 µm thick and 100 mm wide. This amorphous alloy exhibited tensile strength of 1,641 MPa, yield strength of 1,541 MPa, elongation of 1% and elastic modulus of 98GPa. The bulk concentration, resistivity, and mobility values are midway between general heavy doping ceramics and metals, and they are about 100 times weaker than ordinary metals, so they are close to Si and have good electrical conductivity. In addition, folding tests were conducted at extreme temperatures, withstanding 150,000 times at –20°C, 300,000 times at 24°C, and 150,000 times at 60°C, with no folding defects observed. These results demonstrate the excellent durability and reliability of the Zr-14Cu-7.5Ni-2.6Al wide ribbon alloy and suggest the possibility of developing electronic products using this alloy.

Zr-14Cu-7.5Ni-2.6Al, Melt spinning, Wide width, Amorphous ribbon, Electronic products