한국주조공학회

14 cm length Al-15Cu-1Mg alloys have been directionally solidified in 3 mm diameter alumina tubes in a furnace moved with a constant velocity V=12 cm/hr under various furnace temperatures of 660, 710 and 760℃. By analysing the evolution of the temperature profiles along the alloy length during the solidification, the growth characteristics such as the position of the solid/liquid interface, the local growth velocity (R) and the temperature gradient at the solid/liquid interface (G) have been determined. The effects of the furnace temperature on the growth behavior have been investigated by the comparison of R and G values for each temperature. Under the furnace temperature of 760℃, steady state growth region was observed for the latter half of the growth period.