Al-15Cu-lMg alloys have been directionally solidified in 3mm diameter alumina tubes under the conditions of 760℃ of furnace temperature and 12 cm/hr of furnace moving velocity(V). By analyzing the evolution of the temperature profiles along the alloy length, the position of the solid/liquid interface, temperature gradient(G) and local growth velocity (R) were determined. These growth characteristics were compared for 6, 10, 14 cm length alloys. Steady state growth region was obtained in 15 cm length alloy, not in 6, 10 cm.