한국주조공학회

For Pb-20wt%Cu alloys, severe macrosegregation due to density difference of the resulting phases in normal directional solidification has been minimized and a uniformly aligned dendritic structure has been produced by axially rotating the sample of 5mm diameter in conjunction with horizontal directional solidification. Under the constant growth velocity of 20μм/sec, increasing the rotation rate from 0.18 to 12rpm results in a transition from an aligned columnar to an equiaxed Cu-dendritic structure. With a constant rotation rate of 0.18rpm, increasing the growth velocity from 10 to 50μм/sec also has promoted a transition from columnar to equiaxed structure.