한국주조공학회

This study has been carried out to investigate into the difference of rolling life and rolling wear characteristics for various gray cast iron under unlubricated dry rolling condition by amsler type wear test with 9.09% sliding.The results obtained from this study are summerized as follows: 1) It has been found that the amount of rolling wear id decreased when tensile strength and hardness are low, and then the rolling life up to generation of abnormal wear is conspicuously increased. 2) At the given condition the amount of rolling wear has been found to decrease as carbon equivalent of gray cast iron increases and resistance of crack propagation is an important factor on improvement of wear characteristics. 3) The amount of rolling wear is increased with increasing rolling revolution and wear of gray cast iron under dry rolling condition is characterized by three modes; initial wear, stationary wear and abnormal wear. 4) It has been found that the amount of rolling wear is increased with increasing maximum compressive stress and extremely increased when maximum compressive stress is over 59.1㎏.f/mm