한국주조공학회

The influence of columnar dendirtes on the mechanical properties of Al-1% Cu alloys as unifirectionalloy solidified under the conditions of controlled crystal growth rate (R) and temperature gradient (G) was investigated. And the change of metallography and mechanical properties when unifirectionalloy solidified alloys and cast alloys were cold-rolled from 10% to 90% in reduction ratio was studied. The results are as follows: 1. The elongation and yield strength of unifirectionalloy solidified alloy are higher then those of cast alloy, but there is a little decrease in ultimate tensile strength. 2. The metallography and mechanical properties are changeable with the primary arm spacings when the unidirectionalloy solidified alloys were cold- rolled from 10% to 90% in reduction ratio. An alloy with larger primary arm spacings was easily changeable in metallography and mechanical properties when it was cold-rolled. 3. The tensile strength of transversely cold-rolled to 90% in reduction ratio was higher then that of longitudionalloy cold-rolled to 90% in reduction ratio. In the case, the fractorgraphs of fractured surface showed that the cast alloy and the unifirectionalloy solidified alloy was ductile-fractured, but the surface of transversely cold-rolled to 90% reduction of unidirection alloy solidified was slip plane qracture.